2mm Translucent Green Coloured Acrylic Sheet extruded perspex plate
1. Description of Translucent Green Acrylic Sheet
The extruded sheet has lower molecular weight, slightly weaker mechanical properties and higher flexibility, which is beneficial to bending and thermoforming, and has a shorter softening time. At the same time, the thickness tolerance of the extruded sheet is smaller than that of the cast sheet. Due to the large-scale automatic production of extruded sheets, the diversity of product colors and specifications is limited to a certain extent.
2. Parameter of Translucent Green Acrylic Sheet
| PROPERTIES | VALUES | RULES |
| Density | 1.19 g/cm3 | ISO 1183-1:2012 Method A |
| Rockwell Hardness | 112L | ISO 2039-2:1999 |
| Tensile Modulus | 3150MPa | EN ISO 527:2012 |
| Tensile Strength | 80.0MPa | EN ISO 527:2012 |
| Tensile Strain at Break | 3.2% | EN ISO 527-1:2012 |
| Water Absorption | 0.20% | ISO 62:2008 Method 1 |
| Total Luminous Transmittance | 93.4% | ISO 13468-1:1996 |
| Vicat Softening Temperature | 105℃ | ISO 306:2013 Method B50 |
| Light Ageing Test- UV Exposure | Grey scale: 5 | ISO 4892-3:2016 Cycle 1 |
| Mean Coefficient of Linear Thermal Expansion | 72×10-6 K-1 | ISO 11359-1:2014 |
| Compressive Stress at Yield | 129MPa | EN ISO 604:2003 |
| Flexural Strength | 120MPa | ISO 178:2013 |
| Compressive Yield Strength | 111MPa | ASTM D695-15 |
| Compressive Modulus | 3450MPa | ASTM D695-15 |
| Shear Strength | 59.7MPa | ASTM D732-17 |
| Deflection Temperature under Load | 100.2℃ | ASTM D648-18 Method B |
| Modulus Elasticity | 2810MPa | ASTM D695-15 |
3. Translucent Green Acrylic Sheet Types
4.Translucent Green Acrylic Sheet Application
|
|
| Brand Name: | XH |
| Model Number: | XH 362 |
| MOQ: | 50pcs |
| Price: | 2.835USD per KG |
| Packaging Details: | 1500kg/Tray |
| Payment Terms: | T/T, Western Union |
2mm Translucent Green Coloured Acrylic Sheet extruded perspex plate
1. Description of Translucent Green Acrylic Sheet
The extruded sheet has lower molecular weight, slightly weaker mechanical properties and higher flexibility, which is beneficial to bending and thermoforming, and has a shorter softening time. At the same time, the thickness tolerance of the extruded sheet is smaller than that of the cast sheet. Due to the large-scale automatic production of extruded sheets, the diversity of product colors and specifications is limited to a certain extent.
2. Parameter of Translucent Green Acrylic Sheet
| PROPERTIES | VALUES | RULES |
| Density | 1.19 g/cm3 | ISO 1183-1:2012 Method A |
| Rockwell Hardness | 112L | ISO 2039-2:1999 |
| Tensile Modulus | 3150MPa | EN ISO 527:2012 |
| Tensile Strength | 80.0MPa | EN ISO 527:2012 |
| Tensile Strain at Break | 3.2% | EN ISO 527-1:2012 |
| Water Absorption | 0.20% | ISO 62:2008 Method 1 |
| Total Luminous Transmittance | 93.4% | ISO 13468-1:1996 |
| Vicat Softening Temperature | 105℃ | ISO 306:2013 Method B50 |
| Light Ageing Test- UV Exposure | Grey scale: 5 | ISO 4892-3:2016 Cycle 1 |
| Mean Coefficient of Linear Thermal Expansion | 72×10-6 K-1 | ISO 11359-1:2014 |
| Compressive Stress at Yield | 129MPa | EN ISO 604:2003 |
| Flexural Strength | 120MPa | ISO 178:2013 |
| Compressive Yield Strength | 111MPa | ASTM D695-15 |
| Compressive Modulus | 3450MPa | ASTM D695-15 |
| Shear Strength | 59.7MPa | ASTM D732-17 |
| Deflection Temperature under Load | 100.2℃ | ASTM D648-18 Method B |
| Modulus Elasticity | 2810MPa | ASTM D695-15 |
3. Translucent Green Acrylic Sheet Types
4.Translucent Green Acrylic Sheet Application